Feedstock material behaviour in thermal spraying process under different parameters is essential in producing repeatable and controllable coatings. Article reviews three regimes of spraying, with a focus on the wear behaviour under the different conditions. RocDur 37 was selected as feedstock material. Regimes applying different feed were used: 1.43 cm/s (A), 1.85 cm/s (B), 0.88 cm/s (C); rotation speed - 1.33 s−1. Wear was tested on the contactsliding, edge-wear and abrasive-wear machines. Regimes B and C showed lower wear in contact-sliding and edge-wear. Hydro-abrasive test showed similar wear of coatings obtained using all parameters, it can be concluded that RocDur 37 coatings are suitable for work in abrasive conditions. In this type of wear technological parameters do not affect wear. The optimum technological regimes: rotation speed 1.33 s−1, longitudinal feed 0.88 cm/s, and 11 passes.