Abstract A series of azo-based diblock copolymers (DBCs) with various compositions were successfully synthesized via reversible addition-fragmentation chain transfer (RAFT) polymerization in anisole with PCAEMA-CTA (macro-CTA), DOPAM (new acrylamide monomer) and AIBN (initiator). Kinetic studies on diblock copolymerization manifested a controlled/living manner with good molecular weight control. Structures and properties of monomers and DBCs were determined by 1H nuclear magnetic resonance (NMR), differential scanning calorimetry (DSC) and gel permeation chromatography (GPC). Liquid crystalline (LC) phases and morphological properties were investigated using optical polarizing microscope (OPM), atomic force microscopy (AFM), scanning electron microscopy (SEM) and small-angle X-ray scattering (SAXS). Experimental results demonstrated that the prepared PCAEMA-CTA and DBCs possessed low polydispersity index (≤1.37). All DBCs revealed sharp endothermic transition peaks corresponding to the smectic-to-nematic phase. DBCs with high azo contents showed batonnet textures of the smectic phase whereas DBCs of low azo segments displayed threaded textures of the nematic phase. DBC with 49 wt% of azo side-chains generated a lamellar compared to DBCs with low azo block (≤41 wt%) or non-azo block (≤38 wt%) which produced hexagonal-type nanostructures. In addition, all DBCs exhibited reversible trans-cis photoisomerization behavior under UV irradiation and dark storage at different intervals of time.