Abstract Poplar wood samples (2×2×2 cm3) were vacuum/pressure impregnated in alcoholic solution with 2-hydroxyethyl methacrylate (HEMA) and 3-(methacryloxy)propyltrimethoxysilane (MAPTES) in a mass ratio of 3/1 in the presence of catalytic… Click to show full abstract
Abstract Poplar wood samples (2×2×2 cm3) were vacuum/pressure impregnated in alcoholic solution with 2-hydroxyethyl methacrylate (HEMA) and 3-(methacryloxy)propyltrimethoxysilane (MAPTES) in a mass ratio of 3/1 in the presence of catalytic amounts of azobisisobutyronitrile (AIBN). Because of their good solubility and permeability, the HEMA/MAPTES precursors evenly penetrate the poplar cell wall. The impregnated samples were heated at 75°C for 8 h, followed by a heating period at 103±2°C for 8 h, in the course of which an in situ polymerization occurred in the cell wall. The modified wood was characterized by Fourier transform infrared (FTIR) and Raman spectroscopy, X-ray diffraction (XRD) and scanning electron microscopy (SEM). Moreover, the dimensional stability of the modified wood was measured and found to be considerably improved.
               
Click one of the above tabs to view related content.