Abstract The effect of the addition of 2CaO·SiO2 solid particles on dephosphorization behavior in carbon-saturated hot metal was investigated. The research results showed that the addition of 2CaO·SiO2 particles have little influence on desilication and demanganization, and the removal of [Si] and [Mn] occurred in the first 5 min with different conditions where the contents of 2CaO·SiO2 particles addition for the conditions 1, 2, 3, 4, and 5 are 0, 2.2, 6.4, 8.6, and 13.0 g, respectively. The final dephosphorization ratios for the conditions 1, 2, 3, 4, and 5 are 61.2%, 66.9%, 79.6%, 63.0%, and 78.1%, respectively. The dephosphorization ratio decreases with the increase of 2CaO·SiO2 particles in the first 3 min. The reason for this is that the dephosphorization process between hot metal and slag containing C2S phase consisted of two stages: Stage 1, [P] transfers from hot metal to liquid slag and Stage 2, the dephosphorization production (3CaO·P2O5) in liquid slag reacts with 2CaO·SiO2 to form C2S–C3P solid solution. The increase of 2CaO·SiO2 particles increases the viscosity of slag and weakens the dephosphorization ability of the stage 1. The SEM and XRD analyses show that the phase of dephosphorization slag with the addition of different 2CaO·SiO2 particles is composed of white RO phase, complex liquid silicate phase, and black solid phase (C2S or C2S–C3P). Because the contents of C2S–C3P and 2CaO·SiO2 in slag and the dephosphorization ability of the two stages are different, the dephosphorization ability with different conditions is different.