The withdrawal strength of plain dowels with nominal diameter of 8 mm was compared with the spiral dowels manufactured from beech (Fagus sylvatica L.) and oak wood (Quercus robur L.). The test specimens were tested after conditioning at relative humidity (RH) 25%, 45%, 65%, and 85% at a constant temperature of 20 °C. Therefore, the influence of relative humidity (respective moisture content), dowel structure, and wood species of the dowels on the withdrawal strength was determined. The structure and low humidity (RH 25%) caused the highest strength (8.6 MPa) of spiral dowels. Compared to plain dowels, the higher withdrawal strength of spiral dowels was statistically significant. Adversely, the lowest withdrawal strength was found for plain beech dowels (3 MPa), which, in addition to higher relative humidity (RH 85%), was also caused by a combination of plain structure and greater diameter of the dowels, thereby decreasing the amount of adhesive in the bonded joint. The influence of the wood species of the dowels was not statistically significant overall.