The plastic debris that washes ashore and litters the shoreline often undergoes weathering under sunlight exposure, such that it fragments to form nanoplastics and microplastics, but the fragmentation rate for many thermoplastics is unknown. In this study, three major thermoplastics were exposed to simulated sunlight in an accelerated weathering chamber to evaluate the speed of photooxidation-induced fragmentation. The initiation of photooxidation-induced fragmentation extrapolated from the accelerated weathering chamber to real sunlight exposure in South Korea followed the order of PS (1.3 × 107 particles/cm2/0.9 years) > PP (5.4 × 106 particles/cm2/1.8 years) > LDPE (1.4 × 107 particles/cm2/3.7 years). The surface cracks created by photooxidation were not directly reflected in the initiation of fragmentation of thermoplastics. The initiation of fragmentation was faster in PS than other polymers, but the total abundance of particles produced, and increasing ratio (exposure/non-exposure) were comparable or lower than those of PP. The increasing ratio pattern between nanoplastics and small microplastics of PP differed noticeably from other polymers. The initiation of nanoplastic and small-microplastic fragmentation determined in this study will be useful for the further estimation of secondary microplastic production by weathering and thus for decision-making regarding methods for the timely removal of plastic litter in the environment.