?-Si3N4 nanowires with diameters of 100-180 nm (Si3N4-W1) and 420-510 nm (Si3N4-W2) were synthesized by a modified chemical vapour deposition (CVD) method and their microstructure changes after high-temperature oxidation were… Click to show full abstract
?-Si3N4 nanowires with diameters of 100-180 nm (Si3N4-W1) and 420-510 nm (Si3N4-W2) were synthesized by a modified chemical vapour deposition (CVD) method and their microstructure changes after high-temperature oxidation were studied. The results showed that both Si3N4 nanowires were not significantly oxidized when the temperature was lower than 900?C. However, the Si3N4-W1 microstructure began to change significantly after oxidation at 1200?C, while the Si3N4-W2 microstructure remained almost unchanged. Moreover, the Si3N4- W1 and Si3N4-W2 nanowires oxidized significantly after treatment at 1400?C, with weight gain of 26.4% and 13.7%, respectively.
Journal Title: Processing and Application of Ceramics
Year Published: 2023
Link to full text (if available)
Share on Social Media: Sign Up to like & get
recommendations!