This article deals with the effect of manganese that is the most applied element to eliminate the negative effect of iron in the investigated alloy AlSi7Mg0.3. In this time are several methods that are used for elimination harmful effect of iron. The most used method is elimination by applying the additive elements, so-called iron correctors. The influence of manganese on the morphology of excluded ironbased intermetallic phases was analysed at various iron contents (0.4; 0.8 and 1.2 wt. %). The effect of manganese was assessed in additions of 0.1; 0.2; 0.4 and 0.6 wt. % Mn. The morphology of iron intermetallic phases was assessed using electron microscopy (SEM) and EDX analysis. The increase of iron content in investigated alloys caused the formation of more intermetallic phases and this effect has been more significant with higher concentrations of manganese. The measurements carried out also showed that alloys with the same Mn/Fe ratio can manifest different structures and characteristics of excluded iron-based intermetallic phases, which might, at the same time, be related to different resulting mechanical properties.