The fatigue failure of steel 20 at low temperatures is considered. Strain hardening of the surface layers is found to occur in adiabatic conditions at low temperatures. That increases the… Click to show full abstract
The fatigue failure of steel 20 at low temperatures is considered. Strain hardening of the surface layers is found to occur in adiabatic conditions at low temperatures. That increases the fatigue strength. Fatigue cracks form and grow along the grain boundaries. The influence of impurities on the fatigue failure of low-carbon steel is studied.