Nonstoichiometric (Ti,Co)Ox coatings were prepared using gas-impulse magnetron sputtering (GIMS). The properties of coatings with 3 at.%, 19 at.%, 44 at.%, and 60 at.% Co content were compared to those… Click to show full abstract
Nonstoichiometric (Ti,Co)Ox coatings were prepared using gas-impulse magnetron sputtering (GIMS). The properties of coatings with 3 at.%, 19 at.%, 44 at.%, and 60 at.% Co content were compared to those of TiOx and CoOx films. Structural studies with the aid of GIXRD indicated the amorphous nature of (Ti,Co)Ox. The fine-columnar, homogeneous microstructure was observed on SEM images, where cracks were identified only for films with a high Co content. On the basis of XPS measurements, TiO2, CoO, and Co3O4 forms were found on their surface. Optical studies showed that these films were semi-transparent (T > 46%), and that the amount of cobalt in the film had a significant impact on the decrease in the transparency level. A shift in the absorption edge position (from 337 to 387 nm) and a decrease in their optical bandgap energy (from 3.02 eV to more than 2.60 eV) were observed. The hardness of the prepared films changed slightly (ca. 6.5 GPa), but only the CoOx film showed a slightly lower hardness value than the rest of the coatings (4.8 GPa). The described studies allowed partial classification of non-stoichiometric (Ti,Co)Ox thin-film materials according to their functionality.
               
Click one of the above tabs to view related content.