Adding basalt fiber into concrete can significantly improve its mechanical properties. In order to explore the influence of basalt fiber content on the uniaxial compressive strength and splitting tensile strength of concrete and the mechanism of fiber action, this paper conducts compressive and splitting tensile tests on three kinds of basalt fiber concrete specimens with different fiber content and obtains the relationship between the macro mechanical properties and the fiber content. At the same time, with the help of CT scanning equipment and digital image processing technology, the microstructure of basalt fiber concrete with three groups of fiber content is reconstructed, and the pore, crack, and fiber distribution are quantitatively described using the calculation and processing function of the Avizo reconstruction software. The results show that when the optimal fiber content is 3 kg/m3, the improvement rates of uniaxial compressive strength and splitting tensile strength are 31.9% and 23.7%, respectively. The network structure formed by fiber in concrete has the best compactness and the least number of pores, with an average sphericity of 0.89 and an average pore volume of 20.26 μm3. Through analysis, it was found that the initial defects of basalt fiber concrete exist in the form of pores, and the addition of basalt fiber will destroy the large pore size of concrete, change the pore size distribution, and increase the average sphericity; The distribution of the fiber in the concrete is a three-dimensional network, and the distribution of the fiber in the initial defect distribution area is parallel to the direction of pore arrangement.