We report a possible coexistence of nontrivial topology and antiferromagnetism in the newly discovered compounds EuCdBi2, with magnetic Eu layer locating above and below Bi square net. The X-ray diffraction on single crystals and powder indicats that this 112-type material crystalizes in space group of I4/mmm, the same as SrMnBi2 and EuMnBi2. Our combined measurements of magnetization, electrical transport and specific heat consistently reveal antiferromagnetic (AFM) transition of Eu2+ moments at TN = 20 K. The Eu moments are not saturated under a field of 7 T at 1.8 K. The anisotropic susceptibility suggests the Eu moments lie in the ab plane, and a metamagnetic (MM) transition is observed near 1 T below TN. Large positive magnetoresistance (MR) present for both H ‖ ab and H ‖ c, which are considered to contain part contributions from Dirac bands. Hall measurements show the electron-hole compensation effect is prominent above 100 K, with a crossover of Hall resistance from negative to positive values at ∼150 K. The fitted mobility of electrons is as high as 3250 cm2 V−1 S−1 at 1.8 K. Interestingly, the rapid increase of carrier density and suppression of mobility appear at around TN, indicating non-negligible interaction between Eu moments and electron/hole bands. EuCdBi2 may provide a new platform to investigate the interplay of topological bands and antiferromagnetic order.