This work presents the results of oxidation studies on commercially available Nirosta 4016/1.4016 ferritic steel, which contains 16.3 wt.% chromium, as well as the electrical properties of steel/scale layer systems in order to determine the usefulness of this steel for constructing metallic interconnects in solid oxide fuel cell (SOFC) and solid oxide electrolyzer cell (SOEC) stacks. The E-Brite ferritic steel, consisting of up to 26 wt.% chromium, was chosen as a reference material. High-temperature isothermal oxidation kinetics studies were carried out on both steels at 1073 K for 255, 505, 760 and 1010 h in air atmosphere. These conditions are representative of those present in the cathode compartment of a SOFC and the anode compartment of a SOEC. Area specific resistance (ASR) measurements were performed on steel/scale layer systems, obtained after the previous oxidation of both steels in the above-mentioned conditions, in the air in the temperature range of 573–1073 K using the pseudo-DC four-probe method. On the basis of these studies, complemented by morphology observations, as well as chemical and phase composition analysis of the oxidation products, the usefulness of Nirosta 4016/1.4016 ferritic steel for manufacturing interconnects in energy conversion electrochemical devices operating at 1073 K was confirmed.