The present study envisages the preparation of chromium substituted Nickel ferrite NiCrxFe2−xO4 (x = 0~1.0) powders by a sol-gel auto-combustion method. X-ray diffraction analysis (XRD) showed that the specimens with x > 0.2 exhibited a single-phase spinel structure, and that more content of Cr within a specimen is favorable for the synthesis of pure Ni-Cr ferrites. The lattice parameter decreased with an increase in the Cr concentration. The sample without calcining exhibited a good crystallinity. Scanning Electron Microscopy (SEM) showed the formation of ferrite powders nano-particles, and that the substitution of Cr weakened the agglomeration between the particles. Mössbauer spectra of NiCrxFe2−xO4 showed two normal Zeeman-split sextets that displayed a ferrimagnetic behavior. Furthermore, the spectra indicated that iron was in the Fe3+ state, and the magnetic hyperfine field at the tetrahedral tended to decrease with an increase in the Cr substitution. The saturation magnetization decreased by the Cr3+ ions, and reached a minimum value (Ms = 4.46 emu/g). With an increase in the annealing temperature, the coercivity increased initially, which later decreased.