An allomorph MnO2@MnO2 core-shell nanostructure was developed via a two-step aqueous reaction method. The data analysis of Scanning Electron Microscopy, Transmission Electron Microscopy, X-Ray Diffraction and N2 adsorption-desorption isotherms experiments indicated that this unique architecture consisted of a porous layer of amorphous-MnO2 nano-sheets which were well grown onto the surface of α-MnO2 nano-needles. Cyclic voltammetry experiments revealed that the double-layer charging and Faradaic pseudo-capacity of the MnO2@MnO2 capacitor electrode contributed to a specific capacitance of 150.3 F·g−1 at a current density of 0.1 A·g−1. Long cycle life experiments on the as-prepared MnO2@MnO2 sample showed nearly a 99.3% retention after 5000 cycles at a current density of 2 A·g−1. This retention value was found to be significantly higher than those reported for amorphous MnO2-based capacitor electrodes. It was also found that the remarkable cycleability of the MnO2@MnO2 was due to the supporting role of α-MnO2 nano-needle core and the outer amorphous MnO2 layer.