In this study, Zr0.92Y0.08O2-α(8YSZ) powders were synthesized by the sol-gel method. The chemical physics changes and phase formation temperature of 8YSZ crystal were determined by thermogravimetry analysis and differential scanning… Click to show full abstract
In this study, Zr0.92Y0.08O2-α(8YSZ) powders were synthesized by the sol-gel method. The chemical physics changes and phase formation temperature of 8YSZ crystal were determined by thermogravimetry analysis and differential scanning calorimetry (TGA-DSC). 8YSZ-low melting point glass powder (8YSZ-glass) composite electrolytes with various weight ratios were prepared and calcined at different temperatures. The X-ray diffraction (XRD) patterns of the composite electrolytes were tested. The effects of synthesis temperature, weight ratio, test temperature, and oxygen partial pressure on the conductivities of 8YSZ-glass composite electrolytes, were also investigated at 400–800 °C. The result of the logσ ~ log(pO2) plot indicates that the 8YSZ-20% glass (700 °C) is almost a pure ionic conductor. The oxygen concentration discharge cell illustrates that the 8YSZ-20% glass (700 °C) composite electrolyte is a good oxygen ion conductor.
               
Click one of the above tabs to view related content.