In this investigation, ZrxY2−xVxMo3−xO12 (0 ≤ x ≤ 1.4) is developed and the effects of the substitutions of Zr4+/V5+ for Y3+/Mo6+ in Y2Mo3O12 on the hygroscopicity and thermal expansion property… Click to show full abstract
In this investigation, ZrxY2−xVxMo3−xO12 (0 ≤ x ≤ 1.4) is developed and the effects of the substitutions of Zr4+/V5+ for Y3+/Mo6+ in Y2Mo3O12 on the hygroscopicity and thermal expansion property are investigated. For the smaller substitution content (x ≤ 0.5), their crystal structures remain orthorhombic, while there is crystal water still in the lattice. The linear coefficients of thermal expansions (CTEs), for x = 0.1, 0.3, 0.5, and 0.7, are about −4.30 × 10−6, −0.97 × 10−6, 0.85 × 10−6, and 0.77 × 10−6 K−1, respectively, from 476 to 773 K, which means that the linear CTE could be changed linearly with the substitution content of Zr4+/V5+ for Y3+/Mo6+ in Y2Mo3O12. As long as the substitution content reaches x = 1.3/1.4, almost no hygroscopicity and low thermal expansion from room temperature are obtained and are discussed in relation to the crystal structure and microstructure.
               
Click one of the above tabs to view related content.