The Effect of Ca Dopant on the Electrical and Dielectric Properties of BaTi4O9 Sintered Ceramics

Photo from wikipedia

The current research examines the impact of Ca2+ substitution on the phase and electrical properties of (Ba1−xCax)Ti4O9, (x = 0.0, 0.3, 0.6, and 0.9) sintered pellets synthesized by solid-state reaction… Click to show full abstract

The current research examines the impact of Ca2+ substitution on the phase and electrical properties of (Ba1−xCax)Ti4O9, (x = 0.0, 0.3, 0.6, and 0.9) sintered pellets synthesized by solid-state reaction method. The as-synthesized samples were analyzed using X-ray diffraction (XRD) and impedance spectroscopy. The emergence of orthorhombic phase fit into space group Pnmm was revealed by XRD, and the addition of Ca resulted in a considerable shift in grain size. Dielectric properties were determined using an impedance spectroscopy in a wide frequency range from 1MHz to 3 GHz. The dielectric properties i.e., dielectric constant (εr) and dielectric loss (tanσ), were measured at 3 GHz frequency. The frequency-dependent parameters such as conductivity, dielectric constant, and dielectric loss indicated that the relaxation process is a Maxwell–Wagner type of interfacial polarization. The improved dielectric properties and low energy loss have made (Ba1−xCax)Ti4O9 a prominent energy storage material. This study provides the possibility to improve its dielectric properties and reduce energy loss, making it an excellent energy storage material.

Keywords: energy; effect dopant; dielectric properties; spectroscopy; loss

Journal Title: Materials
Year Published: 2021

Link to full text (if available)


Share on Social Media:                               Sign Up to like & get
recommendations!

Related content

More Information              News              Social Media              Video              Recommended



                Click one of the above tabs to view related content.