Friction stir lap welding (FSLW) is expected to join the hybrid structure of aluminum alloy and steel. In this study, the Al-Mg-Si aluminum alloy and 301L stainless steel were diffusion bonded by FSLDW with the addition of 0.1 mm thick pure Zn interlayer, when the tool pin did not penetrate the upper aluminum sheet. The characteristics of lap interface and mechanical properties of the joint were analyzed. Under the addition of Zn interlayer, the diffusion layer structure at lap interface changed from continuous to uneven and segmented. The components of the diffusion layer were more complex, including Fe-Al intermetallic compounds (IMCs), Fe-Zn IMCs and Al-Zn eutectic. The largely changed composition and thickness of uneven and segmented diffusion layer at the lap interface played a significant role in the joint strength. The tensile shear load of Zn-added joint was 6.26 kN, increasing by 41.3% than that of Zn-not-added joint. These two joints exhibited interfacial shear fracture, while the Zn interlayer enhanced the strength of diffusion bonding by extending the propagation path of cracks.