In this study, Friction plug welding (FPW) for 8 mm thickness AA2219-T87 sheets were carried out, and defect-free joints were obtained. The geometric size of plug and plate hole, rotational speed and welding force exhibit significant effects on the weld formation. Meanwhile, it is concluded that significant inhomogeneity of microstructure and mechanical properties exists in FPW joints. The recrystallization zone has the highest mechanical properties owing to the fine equiaxed grains and uniformly distributed θ precipitates. The entire plug, thermo-mechanically affected zone and nugget thermo-mechanically affected zone closed to the bonding interface are significantly softened due to the deformation of the grains and θ’ precipitate dissolution. The ultimate tensile strength (UTS) and elongation of the FPW joints can reach 359 MPa and 7.3% at 77 K and 305 MPa and 5% at 298 K, respectively.