LAUSR

In the present work, the surface integrity and flank wear of uncoated cermet inserts in dry turning of AISI 1045 steel were evaluated. Three-dimensional techniques were used to assess the surface roughness. Previously, finite element analysis was carried out to predict the cutting forces and heat distribution in the chip formation region. Cutting speed and feed were the parameters varied in the experiments. Feed is decisive in the final quality of the turned surface and cutting speed had little influence on this aspect. The surface was significantly damaged with the progression of the insert flank wear. Considering an average flank wear VBB of 0.1 mm, a tool life of 35 min was achieved using a cutting speed of 175 m/min, and of 23 min for a cutting speed of 275 m/min. Abrasive wear was predominant during the experiments. No microstructure defects were observed, as well as crack propagation or accentuated deformations near the machined surface region. Therefore, the dry turning of 1045 steel with cermet inserts route has proven extremely viable from the standpoints of tool life, surface integrity, chip formation, and sustainability.