In this work, 3-3 type porous lead zirconate titanate (PZT) ceramics were fabricated by incorporating particle-stabilized foams using the gel-casting method. Then, Portland cement pastes with different water/cement ratios (w/c) were cast into the porous ceramics to produce cement-based piezoelectric (PZT-PC) composites. The effects of w/c on phase structure, microscopic morphology, and electrical properties were studied. The results showed that the amount of hydrated cement products and the density of the PZT–PC composites increased with the increase of w/c from 0.3 to 0.9 and then decreased till w/c achieved a value of 1.1. Correspondingly, the values of both εr and d33 increased with the density of the PZT–PC composites, resulting in less defects and greater poling efficiency. When w/c was maintained at 0.9, the 3-3 type cement-based piezoelectric composites presented the greatest Kt value of 40.14% and the lowest Z value of 6.98 MRayls, becoming suitable for applications in civil engineering for structural health monitoring.