Influence of Annealing Time on Microstructure and Mechanical Properties of Al-14.5Si Alloy Prepared by Super-Gravity Solidification and Cold-Rolling

Photo from wikipedia

In this paper, super-gravity solidification and cold-rolling were utilized to obtain Al-14.5Si alloys. The influence of annealing time on microstructure and mechanical properties of Al-14.5Si alloys was investigated. Our results… Click to show full abstract

In this paper, super-gravity solidification and cold-rolling were utilized to obtain Al-14.5Si alloys. The influence of annealing time on microstructure and mechanical properties of Al-14.5Si alloys was investigated. Our results indicated that high elongation was achieved by super-gravity solidification due to the submicron eutectic Si, making it possible to undertake the conventional cold-rolling. The yield strength (~214 ± 11 MPa) was significantly enhanced (~68.5%) after cold-rolling mainly due to high dislocation density. The coarsening of eutectic Si could be observed during annealing, which resulted in a decrease in yield strength. The elimination of internal stress and lattice distortion during annealing led to a decrease in micro-cracks/voids beneath the fracture surface during tensile testing, which in turn enhanced the elongation.

Keywords: gravity solidification; super gravity; cold rolling; solidification cold

Journal Title: Materials
Year Published: 2022

Link to full text (if available)


Share on Social Media:                               Sign Up to like & get
recommendations!

Related content

More Information              News              Social Media              Video              Recommended



                Click one of the above tabs to view related content.