The aim of paper is to determine experimentally and numerically the strength characteristics related to the paraglider wing with Fourier transform infrared spectroscopy of applied materials. The applied method consists in theoretical modeling supplemented by the tests of material parameters. First, the set of 10 lightweight fabrics was selected for the tests; the samples are representative for these structures. The materials were tested using the spectroscopy to determine the FTIR spectra. The samples differ in the content of certain characteristic groups. Air permeability change of the materials was determined for the different pressure drops. The air permeability of almost all the analyzed samples was close to zero with the exception of only one material. The tensile strength and elongation at the break of samples were determined on the testing machine. The paraglider samples were characterized by slightly decreased mechanical properties compared to the parachute fabrics. The material characteristics determined during the tests are the input data for the theoretical analysis. The numerical model of the paraglider wing is based on a 3D geometry from previous research, but the stress, strain, and deformation were determined using the ANSYS Structural program and the finite elements method. To determine the strength correctly, we introduce two basic values: the absolute maximal and the representative values that are the biggest repetitive values of stress, strain, and deformation. The stress value was determined by the main factors: (i) the thinner the material, the bigger the stresses that were accumulated; (ii) the stronger the material, the bigger the stresses that were accumulated. The results are similar for all materials and differ mainly by the values. The biggest stresses were observed inside the material contacting the ribs, whereas the biggest deformation and strain were in the regions between ribs, and the smallest were in the contact areas with the fixed supports. Their highest intensity was observed on the leading edge of the paraglider. We conclude that the obtained stresses were far from the breaking level for the wing.