Simulation of Inclusion Particle Motion Behavior under Interfacial Tension in Continuous Casting Mold

Photo from wikipedia

Inclusions entrapped by the solidifying front during continuous casting adversely affect the properties of the final steel products. In this study, we investigated the effect of the interfacial tension due… Click to show full abstract

Inclusions entrapped by the solidifying front during continuous casting adversely affect the properties of the final steel products. In this study, we investigated the effect of the interfacial tension due to surfactant concentration, particularly sulfur, on alumina inclusion motion behavior during molten steel solidification in a continuous casting mold. A two-dimensional numerical model was developed in Ansys Fluent software to simulate the inclusion motion in a continuous casting mold. Further, the impacts of different values of the alumina inclusion diameter, sulfur concentration, and melt temperature were studied to understand the inclusion motion behavior. The inclusion diameter affected the inclusion distribution throughout the domain. The alumina inclusion entrapment percentage varied in the case of sulfur mixing (using an empirical relationship for modeling). It was found that the removal percentage varied according to the sulfur concentration. The addition of sulfur at concentrations from 10 ppm to 70 ppm resulted in a 4% increase in the removal of alumina inclusions (trapped in the solidifying shell), except for the 100-ppm case. Smaller-sized inclusion particles had a 25% higher chance of entrapment at the top level of the mold. Under the effect of a higher surface tension gradient between inclusions and the melt, the predicted findings show that inclusions were vulnerable to engulfment by the solidification front.

Keywords: casting mold; tension; inclusion; continuous casting; motion behavior

Journal Title: Materials
Year Published: 2022

Link to full text (if available)


Share on Social Media:                               Sign Up to like & get
recommendations!

Related content

More Information              News              Social Media              Video              Recommended



                Click one of the above tabs to view related content.