LAUSR

In this work, the external longitudinal magnetic field hybrid metal inert gas welding (M-MIG) additive manufacturing method is employed to produce the Ti-6Al-4V alloy part. The effect of process parameters on the droplet transfer formation and microstructure of the part was studied by a high-speed camera, optical microscope, and electron backscattered diffraction. The results showed that a typical short-circuiting transfer was obtained with the wire feeding speed of 2 m/min–4 m/min. An external longitudinal magnetic field had an obvious effect on the arc shape. The uniform formation of the deposition layer was obtained with the wire feeding speed of 4 m/min. The width of M-MIG deposition layer was greater than that of the MIG, and the width of M-MIG deposition layer was increased with the increase of the magnetic excitation current. The microstructure of the deposition layer was mainly comprised of acicular martensite α’ and massive martensite αm. In addition, the β grain size in the M-MIG was less than that of the MIG. The average microhardness of the MIG deposition layer was 281.6 HV, which was less than that of M-MIG.