A CoCrCuFeNi high-entropy alloy was successfully welded in this study using fiber laser welding. The effects of the welding parameters on the microstructure and mechanical properties were studied. Three zones were formed: the fusion zone, partial melting zone, and base metal. The base metal exhibited a typical dendrite structure, and the Cu element segregated in the interdendrite. The fusion zone consisted of fine equiaxed crystals and columnar crystals with the same crystalline structure as the base metal. The fusion zone exhibited minimal compositional microsegregation after laser welding. Electron backscatter diffraction results showed that the low-angle grain boundary fraction in the fusion zone increased. Furthermore, some dislocations and dislocation pile-ups were present in the fusion zone, and the densities of the dislocations and dislocation pile-ups were higher than those of the base metal. The hardness of the fusion zone was considerably higher than that of the base metal, while the ultimate tensile strength and elongation values were lower than those of the base metal for all conditions. The ultimate tensile strength and the elongation increased gradually and then decreased with increasing laser power. The maximum ultimate tensile strength exceeded that of the base metal by 90%.