This study shows the results of Ni replacement with Co in a W-Ni-Co-type tungsten heavy alloy (WHA) in terms of the structure and mechanical properties. Five alloys containing 92 wt. % of tungsten plus Ni and Co changing in the proportions (Co:Ni) of 1:9, 2:8, 3:7, 4:6, and 5:5 were prepared using liquid phase sintering (LPS). The specimens were studied directly after sintering and after solution heat treatment. The tensile strength, yield strength, and elongation were evaluated. The results of tensile tests were supplemented with microhardness measurements of tungsten grains and matrix. Light microscopy was used for the microstructure, and a scanning electron microscope (SEM) equipped with an EDS attachment was applied for the assessment of the fracture mode and chemical microanalysis. It was concluded that the replacement of Ni with Co led to a tensile property increase that was accompanied by a gradual decrease in elongation that started to be critical for a Co:Ni ratio higher than 4:6.