Commonly used S235JR structural steel, generally associated with good weldability, was joined by high-speed friction welding (HSFW). The friction welding tests were performed with a rotational speed of n = 8000 rpm and four different values of the unit pressure in the friction phase (pf) in the range of 64–255 MPa. The obtained joints were subjected to metallographic observations using an optical microscope; in selected zones of friction joints the average grain size was specified in accordance with the EN ISO 643:2012 standard; the hardness of friction joints was measured using the Vickers method. The friction-welded joint with the highest pf was EBSD-investigated. The obtained friction-welded joints resembled an hourglass, and the microstructure of individual zones of the joints differed depending on the height (axis, radius) of the observations. The generated joining conditions resulted in a significant refinement of the microstructure in the friction weld—the average grain size is about 1 µm2 (for base material it was 21 µm2). The highest increase in hardness above 340 HV0.1 was recorded in the friction weld of the welded joint with the lowest used value pressure in the friction phase. Such a sharp increase in hardness can make the resulting friction-welded joint become sensitive to dynamic or fatigue loads. The electron backscatter diffraction (EBSD) investigation confirmed the strong refinement of the microstructure in the friction-welded joint and the occurrence of the phenomenon of dynamic recrystallization (DRX). The friction weld was also characterized by a large share of high-angle boundaries (HAGBs) >80%. These results may indicate that during high-speed friction welding it is possible to create conditions like those obtained during the High-Pressure Torsion (the method used to produce UFG materials) process.