Tensile Deformation Behaviors of Pure Ti with Different Grain Sizes under Wide-Range of Strain Rate

Photo from wikipedia

In this study, pure titanium equivalent to Grade 1 was subjected to tensile tests at strain rates ranging from 10−6 to 100 s−1 to investigate the relationship between its mechanical… Click to show full abstract

In this study, pure titanium equivalent to Grade 1 was subjected to tensile tests at strain rates ranging from 10−6 to 100 s−1 to investigate the relationship between its mechanical properties and its twinning and slip. Deformation properties and microstructures of samples having average grain sizes of 210 μm (Ti-210), 30 μm (Ti-30), and 5 μm (Ti-5) were evaluated. With increasing strain rates, the 0.2% proof stress and ultimate tensile strength increased for all samples; the fracture strain increased for Ti-210, decreased for Ti-5, and changed negligibly for Ti-30. Comparing high (100 s−1) and low (10−6 s−1) strain rates, twinning occurred more frequently in Ti-30 and Ti-210 at high strain rates, but the frequency did not change in Ti-5. The frequency of 1st order pyramidal slip tended to be higher in Ti-30 and Ti-5 at low strain rates. The higher ductility exhibited by Ti-210 at high strain rates was attributed to the high frequency of twinning. In contrast, the higher ductility of Ti-5 at low strain rates was attributed to the activity of the 1st order pyramidal slip.

Keywords: strain rates; deformation; grain sizes; low strain; strain

Journal Title: Materials
Year Published: 2023

Link to full text (if available)


Share on Social Media:                               Sign Up to like & get
recommendations!

Related content

More Information              News              Social Media              Video              Recommended



                Click one of the above tabs to view related content.