LAUSR

The rheological properties and processability at injection molding were studied for bisphenol-A polycarbonate (PC) that was modified by low-density polyethylene (LDPE) having a low shear viscosity. The LDPE addition significantly decreased the steady-state shear viscosity, especially in the high shear rate region. The decrease did not originate from slippage on the die wall but due to interfacial slippage between the PC and dispersed LDPE droplets that deformed to the flow direction to a great extent. As a result of the viscosity decrease, injection pressure largely decreased from 150 to 110 MPa with the addition only 5 wt.% of LDPE. The enhanced flowability also reduced the warpage of the molded product significantly, demonstrating that the processability at injection molding was improved by the addition of LDPE.