Fe/Al composite coatings with compositions of Fe-25 wt.% Al, Fe-50 wt.% Al and Fe-75 wt.% Al were deposited on pure Al and P91 steel plates by a cold spray, respectively. The microstructure of the cross-section of the fabricated coatings was characterized by SEM and EDX. The bonding strength between the coatings and substrates was measured and analyzed. The effects of the Fe/Al ratios and substrate hardness on the deposition behavior were investigated. It was interesting to find fragmented zones in all fabricated coatings, which were composed of large integrated Al particles and small fragmented Al particles. Meanwhile, the fraction of fragmented zones varied with the fraction of the actual Fe/Al ratio. An Fe/Al ratio of 50/50 appeared to be an optimized ratio for the higher bonding strength of coatings. The in situ hammer effect caused by larger and harder Fe particles played an important role in the cold spray process. The substrate with the higher hardness strengthened the in situ hammer effect and further improved the bonding strength.