The hot metal gas forming process can significantly improve the formability of a tube and is suitable for the manufacturing of parts with complex shapes. In this paper, a double wave tube component is studied. The effects of different temperatures (400 °C, 425 °C, 450 °C and 475 °C) and different pressures (1 MPa, 1.5 MPa, 2 MPa, 2.5 MPa and 3 MPa) on the formability of 6063 aluminum alloy tubes were studied. The influence of hot metal gas forming process parameters on the microstructure was analyzed. The optimal hot metal gas forming process parameters of 6063 aluminum alloy tubes were explored. The results show that the expansion rate increases with the increase in pressure. The pressure affects the deformation of the tube, which in turn has an effect on the dynamic softening of the material. The expansion rate of parts also increases with the increase in forming temperature. The increased deformation temperature is beneficial to the dynamic recrystallization of 6063, resulting in softening of the material and enhanced deformation uniformity between grains, so that the formability of the material is improved. The optimum hot metal gas forming process parameters of 6063 aluminum alloy tubes are the temperature of 475 °C and the pressure of 2.5 MPa; the maximum expansion ratio is 41.6%.