LAUSR

The degradation effect of mold on the coating in a hot and humid environment is one of the important factors that cause layer failure. Combined with the wire beam electrode (WBE) and the traditional surface analysis technique, the local biodegradation of the coatings and the corrosion behaviors of metal substrates can be characterized accurately by a WBE. Herein, a WBE was used to study the degradation impact of Talaromyces funiculosus (T. funiculosus) isolated from a tropical rainforest environment on the corrosion of polyurethane (PU) coating. After immersion for 14 days, the local current density distribution of the WBE surface can reach ~10−3 A/cm2 in the fungal liquid mediums but maintains ~10−7 A/cm2 in sterile liquid mediums. The |Z|0.01Hz value of the high current densities area (#85 electrode) was 1.06 × 109 Ω cm2 in a fungal liquid medium after 14 days of immersion. After being attacked by T. funiculosus, the degradation of the PU was more severe, and there were wrinkles, cracks, blisters, and even micro-holes distributed randomly on the surface of electrodes. This resulted from the self-corrosion caused by the T. funiculosus degradation of the coating; the corrosion caused by the electric coupling effect of the coating was introduced. Energy dispersive spectroscopy (EDS) and Raman spectra results showed that the corrosion products were flakey and globular, which consisted of γ-FeOOH, γ-Fe2O3, and α-FeOOH.