Microstructural stability at elevated temperatures is one of the main concerns for the service reliability of aero-engine turbine blades. Thermal exposure, as an important approach to examine the microstructural degradation, has been widely studied in Ni-based single crystal (SX) superalloys for decades. This paper presents a review on the microstructural degradation induced by high-temperature thermal exposure and the associated damage in mechanical properties in some typical Ni-based SX superalloys. The main factors affecting the microstructural evolution during thermal exposure and the influencing factors in the degradation of mechanical properties are also summarized. Insights into the quantitative estimation of the thermal exposure-affected microstructural evolution and the mechanical properties will be beneficial for the understanding and improvement of reliable service in Ni-based SX superalloys.