LAUSR

Background: To evaluate the effect of different experimental staining procedures on color stability and translucency of a nano-hybrid resin-based composite (RBC). Methods: Forty-eight cylindrical-shaped specimens (10 × 2 mm) were prepared with a nano-hybrid RBC (Clearfil Majesty ES-2) and randomly divided in four groups according to the experimental staining procedure: G1) static immersion in a staining solution (coffee) (44 ± 1 °C); G2) staining cycling between coffee (44 ± 1°C) and distilled water (37 ± 1°C) with an experimental staining machine based on Arduino, an Open Source hardware development platform; G3) staining cycles as in G2 + brushing with a low abrasive toothpaste (Relative Dentin Abrasion RDA = 30) (Elmex Sensitive Professional); G4) staining cycles as in G3, with brushing performed with a very strong abrasive toothpaste (RDA = 90) (Lacult Active). Color parameters were recorded at the baseline (T0) after staining procedures (T1) and repolishing (T2) using a spectrophotometer. Color change (∆E00) and translucency (TP, CR) were evaluated. Data were statistically analyzed (p < 0.05). Results: For ∆E00 after staining, Group 1 showed the highest color change and Group 3 the lowest. All groups were significantly different (p < 0.001) except for Group 2 vs. Group 4; after repolishing, Group 1 was significantly higher than Group 3 (p < 0.001), Group 2 (p < 0.001), and Group 4 (p = 0.003); Group 2 was higher than Group 3 (p < 0.001). For TP variable, after staining procedures, Group 2 was significantly higher than all other groups (p < 0.001), and Group 1 was significantly higher than Group 3 (p < 0.001) and Group 4 (p = 0.007). After repolishing, Group 4 was significantly lower than Group 3 (p = 0.008) and Group 2 (p = 0.027). Repolishing procedure significantly reduced color parameters. Conclusions: The investigated staining procedure induced significant differences in color stability and translucency. The use of a very strong abrasive toothpaste (RDA = 90) induced higher color change than a low abrasive one (RDA = 30). Repolishing procedures are able to partially reduce color change induced by artificial staining procedures.