In this study, electrolyte-insulator-semiconductor (EIS) capacitors with Sb2O3/SiO2 double stacked sensing membranes were fabricated with pH sensing capability. The results indicate that Sb2O3/SiO2 double stacked membranes with appropriate annealing had… Click to show full abstract
In this study, electrolyte-insulator-semiconductor (EIS) capacitors with Sb2O3/SiO2 double stacked sensing membranes were fabricated with pH sensing capability. The results indicate that Sb2O3/SiO2 double stacked membranes with appropriate annealing had better material quality and sensing performance than Sb2O3 membranes did. To investigate the influence of double stack and annealing, multiple material characterizations and sensing measurements on membranes including of X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and scanning electron microscopy (SEM) were conducted. These analyses indicate that double stack could enhance crystallization and grainization, which reinforced the surface sites on the membrane. Therefore, the sensing capability could be enhanced, Sb2O3/SiO2-based with appropriate annealing show promises for future industrial ion sensing devices.
               
Click one of the above tabs to view related content.