Gossan ore of sulfide zinc deposit contains abundant zinc, iron, and other metal elements, which is a significant resource with complex components and can be utilized. In this study, a new technology of preparing zinc ferrite from zinc sulfide deposit gossan was proposed. The effects of Al2O3, CaO, and SiO2 in gossan on the formation of zinc ferrite were investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM), and specific surface area and pore size analysis (BET). The results show that the presence of Al2O3 and CaO could hinder the formation of zinc ferrite, while silica had no effect on the formation of zinc ferrite. Under the conditions of the molar ratio of ZnO and Fe2O3 to Al2O3, CaO, and SiO2 of 1:1:1, an activation time of 60 min, and a roasting temperature of 750 °C for 120 min, the products, which had good crystallinity, smooth particle surface, and uniform particle size could be obtained. In addition, compared to the roasted products with Al2O3 and CaO, the specific surface area, pore volume, and pore size of the products with SiO2 were the largest.