Volatile global oil prices, owing to the scarcity of fossil resources, have impacted the cost of producing petrochemicals. Therefore, there is a need to seek novel, renewable chemicals from biomass feedstocks that have comparable properties to petrochemicals. In this study, synthesis, thermal and mechanical properties, and degradability studies of a novel series of sustainable thiophene-based copolyesters like poly(hexylene 2,5-thiophenedicarboxylate-co-bis(2-hydroxyethoxybenzene) (PTBxHy) were conducted via a controlled melt polymerization method. Fourier-transform infrared (FTIR) and nuclear magnetic resonance (1H NMR) spectroscopy techniques elucidated the degree of randomness and structural properties of copolyesters. Meanwhile, gel permeation chromatography (GPC) analysis showed a high average molecular weight in the range of 67.4–78.7 × 103 g/mol. The glass transition temperature (Tg) was between 69.4 and 105.5 °C, and the melting point between 173.7 and 194.2 °C. The synthesized polymers outperformed poly(ethylene 2,5-thiophenedicarboxylate) (PETF) and behaved similarly to polyethylene terephthalate. The copolyesters exhibited a high tensile strength of 46.4–70.5 MPa and a toughness of more than 600%, superior to their corresponding homopolyesters. The copolyesters, which ranged from 1,4-bis(2-hydroxyethyl)benzene thiophenedicarboxylate (TBB)-enriched to hexylene thiophenedicarboxylate (THH)-enriched, offered significant control over crystallinity, thermal and mechanical properties. Enzymatic hydrolysis of synthetized polymers using porcine pancreatic lipase (PP-L) over a short period resulted in significant weight losses of 9.6, 11.4, 30.2, and 35 wt%, as observed by scanning electron microscopy (SEM), with perforations visible on all surfaces of the films. Thus, thiophene-based polyesters with cyclic aromatic structures similar to terephthalic acid (TPA) show great promise as PET mimics. At the same time, PP-L appears to be a promising biocatalyst for the degradation of bioplastic waste and its recycling via re-synthesis processes.