LAUSR

In this paper, a series of Fe3O4/MoS2/NiS composite electrodes were synthesized by a simple coprecipitation method. The influence of different ratio additives (MoS2 and NiS) on the performance of iron anodes for Ni-Fe batteries was systematically investigated. In this paper, the mixed alkaline solution of 6 mol/L NaOH and 0.6 mol/L LiOH was used as electrolyte, and sintered Ni(OH)2 was used as counterelectrode. The experimental results show that the MoS2 and NiS additives can effectively eliminate the passivation phenomena in iron electrodes, reduce the electrode polarization, and increase the reversibility capacity. As a result, the Fe3O4/MoS2/NiS composite electrodes exhibit a high specific capacity, good rate performance, and long cycling stability. Especially, the Fe3O4/MoS2 (5%)/NiS (5%) electrode with a suitable ratio of additives can provide excellent electrochemical performance, with high discharge capacities of 657.9 mAh g−1, 639.8 mAh g−1, and 442.1 mAh g−1 at 600 mA g−1, 1200 mA g−1, and 2400 mA g−1, respectively. This electrode also exhibits good cycling stability.