LAUSR

The limitations of TiO2 as a photocatalyst such as the larger bandgap energy, which only activates under the UV region, give a lower photocatalytic activity. This study reports the role of the N and Pt co-dopant on the modification of the TiO2 photocatalyst for photocatalytic degradation of methylene blue dye under different mode preparations, i.e., sequential and vice-versa modes. The sequential mode preparation of the N and Pt co-dopant TiO2 photocatalyst consisted of the initial preparation of the N-doped TiO2 (N-TiO2) under the calcination method, which was then further doped with platinum (Pt) through the photodeposition process labeled as NPseq-TiO2, while the vice-versa mode was labeled as PNrev-TiO2. About 1.58 wt.% of N element was found in the NPseq-TiO2 photocatalyst, while there was no presence of N element detected in PNrev-TiO2, confirmed through an elemental analyzer (CHNS-O) and (EDX) analysis. The optimum weight percentage of Pt for both modes was detected at about ±2.0 wt.%, which was confirmed by inductively coupled plasma-emission spectroscopy (ICP-OES). The photoactivity under methylene blue (MB) dye degradation of the NPseq-TiO2 photocatalyst was 2 and 1.5 times faster compared to the unmodified TiO2 and PNrev-TiO2, where the photodegradation rates were, ca., 0.065 min−1 and 0.078 min−1, respectively. This was due to the N elements being incorporated with the TiO2 lattice, which was proven by UV-Vis/DRS where the bandgap energy of NPseq-TiO2 was reduced from 3.2 eV to 2.9 eV. In addition, the N generated a stronger PL signal due to the formation of oxygen vacancies defects on the surface of the NPseq-TiO2 photocatalyst. The higher specific surface area as well as higher pore volume for the NPseq-TiO2 photocatalyst enhanced its photocatalytic activity. Moreover, the NPseq-TiO2 showed the lowest COD value, and it was completely mineralized after 7 h of light irradiation. The preparation order did not affect the Pt dopant but did for the N element. Therefore, it is significant to investigate different mode preparations of the N and Pt co-dopant for the modification of TiO2 to produce a good-quality photocatalyst for photocatalytic study under the photodegradation of MB dye.