LAUSR

This paper presents the results of studying the processes of epitaxial growth of germanium on silicon with crystallographic orientation (111) in a wide temperature range. The temperature dependences of the duration of the transition stage from the 7 × 7 to 5 × 5 superstructure and the values of the critical thickness of the transition from two-dimensional to three-dimensional growth in the range from 250 to 700 °C are determined using the reflection high-energy electron diffraction method. It was shown for the first time that the transition time from the 7 × 7 superstructure to 5 × 5 superstructure depends on the temperature of epitaxial growth. The region of low temperatures of synthesis, which has received insufficient attention so far, is also considered.