To improve the poor impact toughness of polypropylene (PP), organo-sepiolite (O-Sep) filled 80/20 (w/w) polypropylene/poly(acrylonitrile-butadiene-styrene) (PP/ABS) nanocomposites were fabricated. The contents of O-Sep were correlated with the morphological, mechanical, and rheological behavior of PP/ABS/O-Sep blends. Scanning electron microscopy (SEM) was applied to study the morphology and thermogravimetric analysis (TGA) was applied to study the thermal stability. Differential scanning calorimetry (DSC) and X-ray diffraction (XRD) were applied to study the crystallinity. The obtained results show that O-Sep enhanced the dispersion of ABS in the PP matrix and increased the crystallinity of blends. The rheological results show that O-Sep could increase the viscosity, storage modulus, and loss modulus of blends. Moreover, the mechanical behavior shows that O-Sep (at proper content) simultaneously increased the tensile modulus, flexural modulus, and impact strength of PP/ABS/O-Sep blends.