Octenyl Succinic Anhydride Modified Pearl Millet Starches: An Approach for Development of Films/Coatings

Photo by wildcatwill9 from unsplash

Pearl millet starches were modified at pH 8.0 using 3.0% octenyl succinic anhydride (OSA), and their pasting, rheological properties, and in vitro digestibility were analyzed. The degree of substitution (D.C.)… Click to show full abstract

Pearl millet starches were modified at pH 8.0 using 3.0% octenyl succinic anhydride (OSA), and their pasting, rheological properties, and in vitro digestibility were analyzed. The degree of substitution (D.C.) of OSA-modified starches varied from 0.010 to 0.025. The amylose content decreased after modification, while the reverse was observed for swelling power. After OSA modification, the pasting viscosities (peak, trough, setback (cP)) of the modified starches increased compared to their native counterparts. G′ (storage modulus) and G″ (loss modulus) decreased significantly (p < 0.05) compared to their native counterparts during heating. Yield stress (σo), consistency (K), and flow behavior index (n) varied from 9.8 to 87.2 Pa, 30.4 to 91.0 Pa.s., and 0.25 to 0.47, respectively. For starch pastes, steady shear properties showed n < 1, indicating shear-thinning and pseudoplastic behavior. The readily digestible starch (RDS) and slowly digestible starch (SDS) contents decreased, while the resistant starch (R.S.) content increased. After OSA treatment, the solubility power of the starches increased; this property of OSA starches speeds up the biodegradability process for the films, and it helps to maintain a healthy environment.

Keywords: succinic anhydride; pearl millet; millet starches; octenyl succinic

Journal Title: Polymers
Year Published: 2022

Link to full text (if available)


Share on Social Media:                               Sign Up to like & get
recommendations!

Related content

More Information              News              Social Media              Video              Recommended



                Click one of the above tabs to view related content.