In this study, three-dimensional (3D) polyvinyl alcohol (PVA)/aligned boron nitride (BN) aerogel framework nanocomposites with high performance were fabricated by a facile strategy. The boron nitride powder was initially hydrolyzed and dispersed with a chemically crosslinked plasticizer, diethyl glycol (DEG), in the PVA polymer system. The boron nitride and DEG/PVA suspensions were then mixed well with different stoichiometric ratios to attain BN/PVA nanocomposites. Scanning electron microscopy revealed that BN platelets were well dispersed and successfully aligned/oriented in one direction in the PVA matrix by using a vacuum-assisted filtration technique. The formed BN/PVA aerogel cake composite showed excellent in-plane and out-of-plane thermal conductivities of 0.76 W/mK and 0.61 W/mK with a ratio of BN/PVA of (2:1) in comparison with 0.15 W/mK for the pure PVA matrix. These high thermal conductivities of BN aerogel could be attributed to the unidirectional orientation of boron nitride nanoplatelets with the post-two days vacuum drying of the specimens at elevated temperatures. This aerogel composite is unique of its kind and displayed such high thermal conductivity of the BN/PVA framework without impregnation by any external polymer. Moreover, the composites also presented good wettability results with water and displayed high electrical resistivity of ~1014 Ω cm. These nanocomposites thus, with such exceptional characteristics, have a wide range of potential uses in packaging and electronics for thermal management applications.