In a particular temperature range, 1, 2-benzo-6-diethylamino-fluorane microcapsules (fluorane microcapsules) exhibit a good color-changing function. For the coating on wood surfaces, embedding fluorane microcapsules, good weather resistance, light retention, color retention, impact resistance, and wear resistance are essential. However, the effect of fluorane microcapsule content on its properties has not been verified. Therefore, in this paper, the orthogonal test is designed with the fluorane microcapsule content, drying temperature, and drying time as test factors to identify the most influential factors. Then, by embedding microcapsules into the waterborne coating on wood substrates, the performance of the waterborne topcoat was investigated. The results show that the color of the waterborne topcoat with fluorane microcapsules on a basswood (Tilia europaea) surface can change between yellow and colorless when the temperature rises and falls, achieving reversible thermochromism. The activation temperature was 32 °C, and the range of discoloration temperature was 30–32 °C. The topcoat with a 15% fluorane microcapsule content had the best comprehensive performance. The color difference was 71.9 at 32 °C, the gloss was 3.9% at 60°, the adhesion grade was 0, the hardness was 2H, the impact resistance was 10 kg·cm, the elongation at the break was 15.56%, and liquid resistance was outstanding. After aging tests, the color difference of the topcoat with 15% fluorane microcapsules was more obvious. The damaged area of the topcoat with the addition of 15% fluorane microcapsules was smaller, indicating it had a better aging resistance. The experimental results lay the foundation for the preparation of intelligence-indicating and decorative waterborne coating.