Advanced research on improving the performance of conductive polymer composites is essential to exploring their potential in various applications. Thus, in this study, the electrical conductivity of multilayer nanofibre membranes composed of polyvinyl alcohol (PVA) with different electroconductive fillers content including zinc oxide (ZnO), multiwalled carbon nanotubes (MWNTs), and Ferro ferric oxide (Fe3O4), were produced via electrospinning. The tensile property and electrical conductivity of monolayer membranes were explored. The results showed that PVA with 2 wt.% MWNTs nanofibre membrane has the best conductivity (1.0 × 10−5 S/cm) and tensile strength (29.36 MPa) compared with other fillers. Meanwhile, the combination of multilayer membrane ZnO/Fe3O4/Fe3O4/MWNTs/ZnO showed the highest conductivity (1.39 × 10−5 S/cm). The parallel circuit and calculation of parallel resistance were attempted to demonstrate the conductive mechanism of multilayer membranes, which can predict the conductivity of other multilayer films. The production of multilayer composites that enhance electrical conductivity and improve conductive predictions was successfully explored.