Storage Life Prediction of Rubber Products Based on Step Stress Accelerated Aging and Intelligent Algorithm

Photo from wikipedia

Compared with the constant stress accelerated aging test, the step stress accelerated aging test reduces the accelerated aging test time by increasing the aging temperature step by step to obtain… Click to show full abstract

Compared with the constant stress accelerated aging test, the step stress accelerated aging test reduces the accelerated aging test time by increasing the aging temperature step by step to obtain the aging failure life of rubber in a shorter time, but its data processing method is not mature enough. In this paper, a simplified step is proposed to process the step stress accelerated aging data. The identification of the acceleration factor is transformed into an optimization problem to avoid the error accumulation problem caused by fitting the data at each temperature. Considering the non-Arrhenius phenomenon in the rubber aging process, a modified Arrhenius equation was used to extrapolate the acceleration factor at low temperatures to calculate the prediction curves for the degradation of polyurethane rubber properties at low temperatures. The life prediction results of the constant stress accelerated aging test and step stress accelerated aging test were compared, and the dispersion coefficient between the two results was between 0.9 and 1. The results obtained by the two methods were in good agreement, which proved the correctness and feasibility of the method used in this paper.

Keywords: stress accelerated; aging test; rubber; accelerated aging; step stress

Journal Title: Polymers
Year Published: 2022

Link to full text (if available)


Share on Social Media:                               Sign Up to like & get
recommendations!

Related content

More Information              News              Social Media              Video              Recommended



                Click one of the above tabs to view related content.