LAUSR

Structural adhesion at high temperature has been a challenge for organic adhesives, and the commercially available adhesives that can work at a temperature above 150 °C is rather limited. Herein, two novel polymers were designed and synthesized via facile strategy, which involves polymerization between melamine (M) and M–Xylylenediamine (X), as well as copolymerization of MX and urea (U). With well-balanced rigid-flexible structures, the obtained MX and MXU resins were proved to be outstanding structural adhesives at a wide range temperature of −196~200 °C. They provided room-temperature bonding strength of 13~27 MPa for various substrates, steel bonding strength of 17~18 MPa at cryogenic temperature (−196 °C), and 15~17 MPa at 150 °C. Remarkably, high bonding strength of 10~11 MPa was retained even at 200 °C. Such superior performances were attributed to a high content of aromatic units, which leads to high glass transition temperature (Tg) up to ~179 °C, as well as the structural flexibility endowed by the dispersed rotatable methylene linkages.