LAUSR

In this study, wood protectants were prepared by using manganese chloride, potassium carbonate, borax and nano colloidal silica sol. Effects of the wood protectants on decay resistance, anti-mold property and fire resistance of Pinus massoniana Lamb. were discussed. The results indicated that the optimal formula of the protectant was composed of 20% colloidal silica sol and 8% modifier (manganese chloride + potassium carbonate + borax). Under this formula, the protectant had good permeability and fluidity, accompanied with synergistic effect between colloidal silica sol and modifier. Pinus massoniana Lamb. treated by the protectant with this formula showed good decay resistance, and its mass loss rates after corrosion by Gloeophyllum trabeum and Coriolus versicolor were respectively about 21% and 19%, lower than those of the control group. This indicated that the preferred samples reached I-level decay resistance according to Chinese Forestry Industrial Standards LY/T 1283-2011. Moreover, Pinus massoniana Lamb. under this formula had good anti-mold property, manifested by 100% resistance to Aspergillus niger V. Tiegh and Trichoderma viride Pers. ex Fr. The treated Pinus massoniana Lamb. also showed good fire resistance with the oxygen indexes before and after leaching respectively at 20.45% and 13.64%, higher than those of the control group. It was concluded that the formulated protectant of this research had not only multiple functions of one dose, but also comprehensive resistances to decay, mold and fire, as well as strong leaching resistance.